真空 ›› 2019, Vol. 56 ›› Issue (4): 49-52.doi: 10.13385/j.cnki.vacuum.2019.04.12

• • 上一篇    下一篇

马氏体沉淀硬化不锈钢真空热处理畸变的研究

王博1, 张忠和1, 王飞宇1, 王帅1, 闫帅1, 崔天龙1, 张忠信2   

  1. 1.沈阳鼓风机集团股份有限公司,辽宁 沈阳 110869;
    2.沈阳创推科技有限公司,辽宁 沈阳 110141
  • 收稿日期:2018-08-20 发布日期:2019-08-22
  • 通讯作者: 张忠和,教授级高工。
  • 作者简介:王博(1982-),男,河南省商丘市人,高级工程师。

Study on Vacuum Heat Treatment Distortions of Martensite Precipitation Hardening Stainless Steel

WANG Bo1, ZHANG Zhong-he1, WANG Fei-yu1, WANG Shuai1, YAN Shuai1, CUI Tian-long1, ZHANG Zhong-xin2   

  1. 1.Shenyang Blower Works Group Corporation, Shenyang 110869, China;
    2.Shenyang Innovation popularize Technology Co., Ltd., Shenyang 110141, China
  • Received:2018-08-20 Published:2019-08-22

摘要: 采用马氏体沉淀硬化不锈钢的C形畸变试样,进行真空热处理及气体保护炉热处理变形量的试验研究,并采用金相显微镜、扫描电镜分析不同变形的畸变试样的显微组织,得出本试验条件下的结论:马氏体沉淀硬化不锈钢真空调整、时效的畸变量小于气体保护炉调整、时效的畸变量;真空热处理炉上部的畸变量略大,但抗畸变性能很好;固溶化工序的畸变大于调整工序的畸变;不同结构尺寸的畸变试样变形差异很大,对提高测试精度很有帮助。本试验的结论对控制真空热处理的畸变具有指导意义。

关键词: 真空热处理, 畸变, 马氏体沉淀硬化不锈钢

Abstract: The C-shaped distorted specimens of martensitic precipitation hardening stainless steel were used to carry out the heat treatment distortion study by vacuum heat treatment and gas shielded furnace heat treatment. The metallographic microscope and SEM were used to analyze the microstructure of specimens with different deformation. The results show that the distortion of martensitic precipitation hardening stainless steel by vacuum adjustment and aging is less than that by gas shielded furnace adjustment and aging.The distortion of the specimens in the upper part of the vacuum furnace is larger than that in the lower part, but the anti-distortion performance is very good. The distortion of solution treatment process is greater than that of the adjustment. Deformation of specimens with different structural sizes varies greatly, which is very helpful for improving the test accuracy. The result of this study is instructive to control distortion of vacuum heat treatment.

Key words: Vacuum heat treatment, Distortion, Martensite precipitation hardening stainless steel

中图分类号: 

  • TG156.95
[1] 孙铭炎,华公平.渗碳齿轮的热处理畸变及其控制技术[J].热处理,2008,23(3):24-31.
[2] 张忠和,蒋申柱,赵亮,等.马氏体时效硬化不锈钢真空热处理的组织和性能[J].真空,2018,55(4):65-68.
[3] 周倩青,翟玉春.高强高韧FV520B马氏体钢的时效工艺优化[J].金属学报,2009,45(10):1249-1254.
[4] 王志坚,尚晓峰. 真空高压气淬炉中淬火气体压力、流速和类型对工件冷却性能影响的数值模拟[J].真空,2011,48(6):76-80.
[5] 张忠和. 真空热处理炉现场检漏的理论分析法[J].真空,2012,49(3):35-37.
[6] 孙枫,王广生,佟小军.航空工业中热处理现状和发展[J].金属热处理,2014,39(1):58-66.
[7] 张素颖,陈敏.充电式锤钻的摆杆轴承真空热处理工艺研究[J].真空,2010,47(2):57-59.
[8] 赵云龙,李运.2024 铝合金获得高强韧性的冷轧真空热处理工艺[J].真空,2014,51(3):53-55.
[9] 张忠和,王飞宇,王全振,等.高灵敏度渗碳淬火畸变试样的研制[J].热处理,2017,32(5):26-30.
[10] 张忠和,王飞宇,张尔康,等.高强度马氏体沉淀硬化不锈钢的低温力学性能[J].金属热处理,2014,39(10):42-46.
No related articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!